Anycubic 3D Printers Settings Phrozen 3D Printers Settings Elegoo 3D Printers Settings Flashforge 3D Printers Settings Wanhao 3D Printers Settings Epax 3D Printers Settings Longer 3D Printers Settings Creality 3D Printers Settings Nova3D Printers Settings Peoply 3D Printers Settings Zortrax 3D Printers Settings
- Digital Jewelry Production
- Digital Dental Production
- Blog
Table of Contents
Power Resins Vintage Resin
Powerresins Vintage resin was developed especially for the direct casting of highly detailed jewelry. Vintage resin has low shrinkage. It ensures good casting quality while not shrinking after 3D printing. You can use it for filigree items as well as surface items.
Powerresins Vintage resin can be used in all types of DLP/LCD 3D printers. It has fast curing properties depending on the 3D printer used.
Material Properties
| Material Properties | Value | Measurement Standard |
| Tensile Strength | 22 MPa | ASTM D638 |
| Flexural Strength | 45 MPa | ASTM D790-02 |
| Flexural Module | 1120 MPa | ASTM D790-02 |
| Shore Hardness | ASTM D2240 | |
| Density | 1.1 g/cm3 @23°C | ASTM D1475 |
| Viscosity | 600-650 mPa.s @23°C | DIN 53211-4 |
| Color | Opaque Green |
- It shows low shrinkage behavior.
- Micro paves claw jewelry offers excellent printing characteristics with sharp details suitable for engraving, highly-detailed figures, or filigree.
- Helps you create lighter jewelry with excellent precision.
- No final curing process is required: It is simply washed with ethyl alcohol and after air drying, it is ready for casting.
Storage
Store this product in tightly closed containers, in a properly ventilated storage area, in dry conditions, away from sparks and open flames.
Avoid exposing the material to direct sunlight.
Shelf life is 1 year after production.
Please refer to the Material Safety Data Sheet for additional information.